| Watsontown Brick Company manufactures high-endurance
chemical resistant brick to ensure our clients get products
that are low-maintenance, long-lasting, resistant to stressors,
and easy to clean. Our chemical resistant bricks are
manufactured to provide exceptional resistance to chemicals
and abrasion for the essential protection you have come
to expect from us. Chemical resistant brick is necessary
to various industrial applications due to the destructive
physical and chemical forces occurring in these environments,
which is why when you invest in Watsontown Brick Company's
chemical resistant brick, you're investing in a lifetime. |
| |
Chemical
Resistant Brick-Red Shale Sizes |
You'll find the right sizes for
a variety of applications at Watsontown Brick. |
 |
 |
 |
 |
 |
 |
Double
Straight
4-1/2"(H)
3-5/8"(D)
8"(L)
|
Thick
Single
A
2-1/4"(H)
4"(D)
8"(L)
|
Thick
Single B
2-1/4"(H)
3-3/4"(D)
7-1/2"(L)
|
Thick
Single C
2-1/4"(H)
3-5/8"(D)
7-5/8"(L)
|
Chamfered
Stretcher
4-1/4"(H)
3-5/8"(D)
8"(L)
C=7-7/8"(L)
|
Chamfered
Header
4-1/4"(H)
3-5/8"(D)
C=3-1/2"(D)
8"(L) |
| C279 |
Chemical Resistant
Masonry Units |
|
ASTM Standard Specs
These units comply with the standard specifications
in ASTM C279 Types I and II
|
| Watsontown Brick Results |
| Unit No. |
Modulus
of Rupture
PSI (MPa)
|
Absorption
2 Hour Boil (%) |
| 1 |
2311 |
(16.0) |
3.8 |
| 2 |
2626 |
(18.1) |
4.2 |
| 3 |
1512 |
(10.4) |
3.9 |
| 4 |
1410 |
(9.7) |
3.5 |
| 5 |
1308 |
(9.0) |
3.6 |
| Avg. |
1833 |
(12.6) |
3.8 |
| Sulfuric Acid Boil
Test - Solubility = 7.46% |
| Industry Requirements Table
1 |
| Designation |
Modulus
of Rupture
(Brick or Tile Flatwise)
minimum PSI (MPa)
|
Water
Absorption
Maximum % by
2 Hour Boiling Test
|
H2SO4
Solubility
Maximum %
Weight Loss
|
Average
of 5
Brick or Tile
Low Individual
|
Average
of 5
Brick or Tile
High Individual
|
Average
of 5
Brick or Tile
|
| Type I |
1250 (8.6) 1000
(6.9) |
6.0 7.0 |
20 |
| Type II |
1250 (8.6) 1000
(6.9) |
4.0 5.0 |
12 |
| Tolerances on Warpage
Table 2 |
| Minimum
Face Dimensions, inches (mm) |
Maximum
Permissible Warpage, inches (mm) |
| 8
and under (.203) and under |
3/32
(2.4) |
| over 8-12 (.203 to
.305), inclusive |
1/8
(3.2) |
| over 12-16 (.306 to
.405), inclusive |
5/32
(4.0) |
|
|
USES
- Petroleum
Refineries
- Acid Tank Farms
- Neutralizing
Tanks
- Absorption
Towers
- Storage Tanks
|
| C410 |
Industrial
Floor Brick |
|
ASTM Standard Specs
These units comply with the standard specifications
in ASTM C410 Types T and H
|
| Watsontown Brick Results |
| Unit No. |
Modulus
of Rupture
PSI (MPa)
|
Absorption
5 Hour Boil (%) |
| 1 |
2311 |
(16.0) |
4.0 |
| 2 |
2626 |
(18.1) |
4.5 |
| 3 |
1512 |
(10.4) |
4.2 |
| 4 |
1410 |
(9.7) |
3.7 |
| 5 |
1308 |
(9.0) |
3.7 |
| Avg. |
1833 |
(12.6) |
4.0 |
|
Sulfuric Acid Boil Test - Solubility = 7.46%
*Size of the lot shall be determined by agreement
between the purchaser and the seller
|
| Industry Requirements Table
1 |
| Designation |
Minimum
Modulus of Rupture
(Brick Flatwise)
Gross Area PSI (MPa)
|
Water
Absorption
Maximum % by
5 Hour Boiling Test
|
Maximum
Mass Loss
by Chemical
Resistance
Test, % |
| Average
of 5 Brick |
Individual |
Average
of 5
Brick |
Individual |
| Type T |
1000 (6.9) |
750 (5.2) |
10 |
12 |
No requirement |
| Type H |
1000 (6.9) |
750 (5.2) |
6 |
7 |
20 |
| Tolerances on Warpage
Table 2 |
| Minimum
Face Dimensions, inches (mm) |
Maximum
Permissible Deviation, inches (mm) |
| Up
to 9 (228.6), inclusive |
1/16
(1.6) |
| Over 9 to 12 (228.6
to 304.8), inclusive |
3/32
(2.4) |
| Permissible Variations
in Dimensions Table 3 |
| Specified Dimensions,
inches (mm) |
Maximum
Permissible Variations in Dimensions between Largest
and Smallest Unit in One Lot,* inches (mm) |
| Up to 2 (50.8), inclusive |
1/16
(1.6) |
| Over 2 to 4 (50.8 to
101.6), inclusive |
1/8
(3.2) |
| Over 4 to 9 (101.6
to 228.6), inclusive |
3/16
(4.5) |
| Over 9 to 12 (228.6
to 304.8), inclusive |
1/4
(6.4) |
|
|
USES
- Chemical
Processing
- Steel Mills
- Power
Generation
- Paper and Pulp
- Smelting and
Refining
|
| C980 |
Industrial Chimney
Lining Brick |
|
ASTM Standard Specs
These units comply with the standard specifications
in ASTM C980 Types
I and II
|
| Watsontown Brick Results |
| Unit No. |
Modulus
of Rupture
PSI (MPa)
|
Absorption
5 Hour Boil (%) |
| 1 |
26290 |
(181.4) |
3.8 |
| 2 |
26510 |
(182.9) |
4.2 |
| 3 |
27320 |
(188.5) |
3.9 |
| 4 |
28480 |
(196.5) |
3.5 |
| 5 |
28830 |
(198.9) |
3.6 |
| 6 |
28480 |
(196.5) |
3.6 |
| 7 |
30940 |
(213.5) |
3.5 |
| 8 |
26330 |
(181.7) |
3.5 |
| 9 |
28340 |
(195.5) |
4.2 |
| 10 |
27170 |
(187.5) |
4.3 |
| Avg. |
27870 |
(192.3) |
3.8 |
| Sulfuric Acid Boil
Test - Solubility = 7.46% |
| Industry Requirements Table
1 |
| Designation |
Minimum
Compressive Strength
Gross Area PSI (MPa)
|
Water
Absorption
Maximum % by
2 Hour Boiling Test
|
Maximum
Average Weight
Loss by H2SO4 Boil Test, % |
| Average
of 10 |
Individual |
Average
of 10 |
Individual |
| Type
I |
8,500
(58.6) |
8000
(55.2) |
6.0 |
7.0 |
20 |
| Type
II |
10,000
(69.0) |
9000
(62.1) |
4.0 |
5.0 |
12 |
| Tolerances on Warpage Table
2 |
| Dimensions |
Dimensions |
| Maximum
Permissible Variations in Dimensions between Largest
and Smallest Brick in a Random Sampling of 10 Bricks,
% |
Warpage |
Maximum
Face and Diagonal Dimensions,
inches (mm)
|
Maximum
Permissible Deviation, inches (mm) |
| Height |
3 |
Up to 9-1/2 (241),
inclusive |
1/8 (3.0) |
| Length |
5 |
|
|
| Width |
5 |
|
|
|
|
USES
- Food Processing
and Packaging
Plants
- Dairies
- Pharmaceutical
Plants
- Beverage Plants
|
|
|
|